High reputation Steel Shot-S230 for Ecuador Manufacturer
Short Description:
FEATURES Size:S230 Diameter: 0.6mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S230 TECHINICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
High reputation Steel Shot-S230 for Ecuador Manufacturer Detail:
FEATURES
Size:S230
Diameter: 0.6mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S230
TECHINICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Garnet: The Ancient Stone Which Beholds Sheer Class
Fast and good quotations, informed advisers to help you choose the correct product that suits all your needs, a short production time, responsible quality control and different services for paying and shipping affairs for High reputation Steel Shot-S230 for Ecuador Manufacturer, The product will supply to all over the world, such as: Iceland, United Arab emirates, Russia, We've been consistently broadening the market within Romania in addition to preparation punching in extra premium quality merchandise connected with printer on t shirt so that you can Romania. Most people firmly believe we've the whole capacity to provide you happy solutions.
By Michelle from Manchester - 2017.06.25 12:48
After the signing of the contract, we received satisfactory goods in a short term, this is a commendable manufacturer.
By Arlene from Denver - 2018.02.12 14:52