Newly Arrival Steel Shot-S390 for Algeria Factories
Short Description:
FEAUTRES Size: S390 Diameter: 1.2mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S390 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Newly Arrival Steel Shot-S390 for Algeria Factories Detail:
FEAUTRES
Size: S390
Diameter: 1.2mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S390
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Garnet: The Ancient Stone Which Beholds Sheer Class
Basic Information About Abrasive Garnet Processing
Our commission should be to provide our customers and consumers with ideal top quality and aggressive portable digital products for Newly Arrival Steel Shot-S390 for Algeria Factories, The product will supply to all over the world, such as: Czech republic, Sydney, Germany, Welcome to visit our company, factory and our showroom where displays various products that will meet your expectation. Meanwhile, it is convenient to visit our website, and our sales staff will try their best to provide you the best service. Please contact us if you need more information. Our aim is to help customers realize their goals. We are making great efforts to achieve this win-win situation.
By Mary from Moscow - 2018.06.26 19:27
Goods just received, we are very satisfied, a very good supplier, hope to make persistent efforts to do better.
By Freda from Egypt - 2018.11.28 16:25