FEATURES Size: S70 Diameter: 0.2mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm Grain Distribution of Steel Shot S70 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Well-designed Steel Shot-S70 to Kenya Manufacturers Detail:
FEATURES
Size: S70
Diameter: 0.2mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm
Grain Distribution of Steel Shot S70
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Garnet: The Ancient Stone Which Beholds Sheer Class
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
"Quality to start with, Honesty as base, Sincere company and mutual profit" is our idea, as a way to build constantly and pursue the excellence for Well-designed Steel Shot-S70 to Kenya Manufacturers, The product will supply to all over the world, such as: Czech Republic, venezuela, New Delhi, We welcome customers from all over the world come to discuss business. We supply high quality products, reasonable prices and good services. We hope to sincerely build business relationships with customers from at home and abroad, jointly striving for a resplendent tomorrow.
By Modesty from Iran - 2018.12.14 15:26
The customer service staff is very patient and has a positive and progressive attitude to our interest, so that we can have a comprehensive understanding of the product and finally we reached an agreement, thanks!
By Dominic from Macedonia - 2017.02.14 13:19