Wholesale price for Steel Shot-S390 to Brazil Factories
Short Description:
FEAUTRES Size: S390 Diameter: 1.2mm Hardness: 40-50HRC(377-509HV) Density: 7.2g/cm3 Grain Distribution of Steel Shot S390 TECHNICAL DATA Name Steel Shot Chemistry (C) 0.70~1.20% (Mn) 0.35~1.20% (Si) 0.40~1.20% (S) ≤0.05% (P) ≤0.05% Average Hardness 40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) Deviation ±3.0HRC(±40HV) Micro Structure Tempered martensite or tempered troostite Density 7.2g/cm3
Wholesale price for Steel Shot-S390 to Brazil Factories Detail:
FEAUTRES
Size: S390
Diameter: 1.2mm
Hardness: 40-50HRC(377-509HV)
Density: 7.2g/cm3
Grain Distribution of Steel Shot S390
TECHNICAL DATA
|
Name |
Steel Shot |
|
|
Chemistry |
(C) |
0.70~1.20% |
|
(Mn) |
0.35~1.20% |
|
|
(Si) |
0.40~1.20% |
|
|
(S) |
≤0.05% |
|
|
(P) |
≤0.05% |
|
|
Average Hardness |
40~50HRC (377-509HV) 52~56HRC (543-620HV) 56~60HRC (620-713HV) |
|
|
Deviation |
±3.0HRC(±40HV) |
|
|
Micro Structure |
Tempered martensite or tempered troostite |
|
|
Density |
7.2g/cm3 |
|
Product detail pictures:
Related Product Guide:
Basic Information About Abrasive Garnet Processing
Low Cost Synthesis of Silicon Carbide and Silicon Nitride
Assume full accountability to fulfill all demands of our purchasers; attain continual advancements by marketing the advancement of our clientele; grow to be the final permanent cooperative partner of purchasers and maximize the interests of purchasers for Wholesale price for Steel Shot-S390 to Brazil Factories, The product will supply to all over the world, such as: Norwegian, Estonia, Puerto Rico, We will not only continuously introduce technical guidance of experts from both home and abroad, but also develop the new and advanced products constantly to satisfactorily meet the needs of our clients all over the world.
By Gladys from Bangalore - 2017.05.02 11:33
It is not easy to find such a professional and responsible provider in today's time. Hope that we can maintain long-term cooperation.
By Lindsay from United Arab emirates - 2018.09.23 18:44